Mirror Hairline Finish Stainless Steel Sheet Plate 405 409 416 420j2

Ask Lasest Price
Brand Name :	TESTE
Model Number :
Supply Ability :	5000Tons Per Months
Price :	Negotiate
Certification :	ISO TUV SGS BIS CE
Payment Terms :	L/C, D/A, D/P, T/T, Western Union, MoneyGram,OA
Delivery Time :	5-15days depend on the quantity

Add to Cart

Product Details
Company Profile

Mirror Hairline Finish Stainless Steel Sheet Plate 405 409 416 420j2

Grade 304 Stainless Steel Sheet

304(1.4301)/304L(1.4307)/304H(1.4948) STAINLESS STEEL

Stainless Steel Grade 304 is the standard 18/8 (18% chrome, 8% nickel) austenitic stainless steel. It is a non-magnetic alloy in the annealed condition, however, becomes magnetic as it is cold worked. It is the most ordinarily utilized of all stainless grades. T304 can be effortlessly welded and is the preferred for many deep drawn, spun or formed parts due to its high ductility.

Stainless Steel Grade 304L has oxidation resistance to a maximum temperature of 1650°F (899°C) continuous without considerable scaling. The maximum temperature for intermittent presentation is 1500°F (816°C). Since 304L is an additional low-carbon variety of 304 it can frequently be utilized in the “as-welded” condition (without annealing), even in severe corrosive conditions, except for applications indicating stress relief. 304L has good welding qualities and can be welded by all standard strategy; however, consideration should be paid to maintain a strategic distance from weld “hot cracking”. To relieve stress during severe forming or spinning welding may be followed by annealing.

Stainless Steel Grade 304H includes a high carbon content making the steel more suitable for utilization in applications where high temperatures are available. The benefit of this grade is that it is an austenitic chromium-nickel steel alloy as well as the greater carbon content distribute to increased tensile and yield strength. The material is recommended for utilizing in ASME pressure vessels in working service above 525° C because of the grade's heat resistant properties.

CHEMICAL COMPOSITION

Element	C	Mn	Si	P	S	Cr	Ni	Fe
302	0.15%	2.0%	0.75%	0.045%	0.03%	17.0~19.0%	8.0~10.0%	Remainder
303	0.10%	2.0%	1.00%	0.040%	0.015%	17.0~19.0%	8.0~10.0%	Remainder
304	0.07%	2.0%	0.75%	0.045%	0.03%	17.5~19.5%	8.0~10.5%	Remainder
304L	0.03%	2.0%	0.75%	0.045%	0.03%	17.5~19.5%	8.0~12.0%	Remainder
304H	0.04~0.10%	2.0%	0.75%	0.045%	0.03%	18.0~20.0%	8.0~10.5%	Remainder
309	0.20%	2.0%	0.75%	0.045%	0.03%	22.0~24.0%	12.0~15.0%	Remainder
321	0.08%	2.0%	0.75%	0.045%	0.03%	17.0~19.0%	9.0~12.0%	Remainder
330	0.08%	2.0%	0.75~1.50%	0.03%	0.03%	17.0~20.0%	34.0~37.0%	Remainder
347	0.08%	2.0%	0.75%	0.045%	0.03%	17.0~19.0%	9.0~13.0%	Remainder

MECHANICAL PROPERTIES

Grade	Tensile Strength (MPa) Min	Yield Strength 0.2% Proof (MPa) Min	Elongation (%in 50mm) Min	Hardness
Grade	Tensile Strength (MPa) Min	Yield Strength 0.2% Proof (MPa) Min	Elongation (%in 50mm) Min	Rockwell B (HR B) Max	Brinell (HB) Max
302	620	275		85	147
303	620	310	30	96	230
304	515	205	40	92	201
304L	485	170	40	92	201
304H	515	205	40	92	201
309	515	205	40	95	217
321	515	205	40	95	217
330	552	207	40	95	217
347	515	205	40	92	201

304/304L/304H COMMON APPLICATIONS

Air Bag Sensors
Clamps
Bellows
Flexible Hoses
Hinges
Cryogenic Components
Surgical Instruments
Pressure Vessels
Oil Well Filter Screen
Hypodermic Needles
Medical Parts
Tubing

Product Tags:


*From:	Your email address is incorrect!
*To:	Qingdao Teste Metal Products Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!